| Miejsce pochodzenia: | China |
| Nazwa handlowa: | HY |
| Orzecznictwo: | ISO9001:2008 |
| Minimalne zamówienie: | 1 tons |
|---|---|
| Cena: | Negotiation |
| Szczegóły pakowania: | Anti rust oil to be applied on material and each rod to be packed in paper sleeve |
| Czas dostawy: | 30days |
| Zasady płatności: | T/T, L/C |
| Możliwość Supply: | 30tons a day |
| Materiał: | Stal mikrostopowa | Nazwa produktu: | Hydrauliczny tłoczysko |
|---|---|---|---|
| Stan powierzchni: | chromowane | Grubość chromu: | 20-30 mikronów |
| Chropowatość powierzchni: | Ra≤0.2mikrona i Rt≤2mikro | Tolerancja średnicy: | f7 |
| High Light: | pręt ze stali nierdzewnej,rura cylindra hydraulicznego,pręt stalowy chromowany CK45; |
||
ISO Approved Chrome Plated Steel Rod CK45 ST52 20MnV6 42CrMo4 40Cr HY4520 HY4700
Detailed Product Description
1. Material: CK45, ST52, 42CrMo4, 40Cr, 20MnV6, HY4520, HY4700
2. We have set up the principle of " high quality, good reputation" and passed the ISO9001:2008 international quality system.
3. Yield strength: Not less than 355 MPa
4. Tensile strength: Not less than 610 MPa
5. Completed manufactured equipments, Advanced inspection apparatus
6. Our quality idea: Next process is customer, excelsior to every process.
Detailed Description
1. CHEMICAL COMPOSITION(%)
|
Material |
C% |
Mn% |
Si% |
S% |
P% |
V% |
Ni |
Cr% |
Mo |
Cu |
|
ck45 |
0.42-0.50 |
0.50-0.80 |
0.17-0.37 |
≤0.035 |
≤0.035 |
|
≤0.25 |
≤0.25 |
|
≤0.25 |
|
ST52 |
≤0.22 |
≤1.6 |
≤0.55 |
≤0.04 |
≤0.04 |
0.02-0.15 |
|
|
|
|
|
20MnV6 |
0.17-0.24 |
1.30-1.70 |
0.10-0.50 |
≤0.035 |
0.035 |
0.10-0.20 |
≤0.30 |
≤0.30 |
|
≤0.30 |
|
42CrMo |
0.38-0.45 |
0.5-0.8 |
0.17-0.37 |
≤0.035 |
≤0.035 |
0.07-0.12 |
≤0.03 |
0.90-1.20 |
0.15-0.25 |
≤0.03 |
|
40Cr |
0.37-0.45 |
0.50-0.80 |
0.17-0.37 |
≤0.035 |
≤0.035 |
|
≤0.3 |
0.80-1.1 |
|
≤0.03 |
|
HY4700 |
0.38-0.45 |
1.20 ~1.60 |
0.30~0.50 |
≤0.035 |
≤0.020 |
0.05～0.15 |
≤0.25 |
0.10～0.20 |
≤0.15 |
0.25 |
|
HY4520 |
0.40 ~0.48 |
0.80 ~1.40 |
0.15 ~0.35 |
≤0.035 |
≤0.035 |
≤0.15 |
≤0.25 |
≤0.25 |
≤0.15 |
≤0.25 |
2. MECHANICAL PROPERTIES
|
Material |
T.S / Rm(MPa) |
Y.S / Rel(MPa) |
A% |
CHARPY |
CONDITION |
|
ck45 |
610 |
355 |
16 |
>41J |
Normalized |
|
ck45 |
800 |
540 |
20 |
>41J |
Q+T |
|
ST52 |
500 |
355 |
22 |
|
Normalized |
|
20MnV6 |
750 |
590 |
12 |
>40J |
Normalized |
|
42CrMo4 |
980 |
850 |
14 |
>47J |
Q+T |
|
40Cr |
1000 |
800 |
10 |
|
Q+T |
3. MICRO ALLOY STEEL
|
Material |
MECHANICAL PROPERTIES |
Surface hardness(HBW) |
|||||
|
Rm(MPa) |
Rel(MPa) |
A% |
Z% |
KU2(J) |
|
||
|
HY4700 |
Φ35 - Φ100 |
900 - 1100 |
≥650 |
≥16 |
≥35 |
≥39 |
270-340 |
|
＞Φ100 - Φ140 |
850 - 950 |
≥600 |
≥16 |
≥35 |
≥39 |
270-340 |
|
|
HY4520 |
Φ40 - Φ100 |
750 - 900 |
≥520 |
≥19 |
≥40 |
≥39 |
230-290 |
|
＞Φ100～Φ140 |
750 - 900 |
≥520 |
≥17 |
≥35 |
≥39 |
230-290 |
|
|
|
|
|
|
|
|
|
|
4. SUPPLY CONDITION
Ground and chrome plated
5. SURFACE ROUGHNESS
Ra≤0.2 micron and Rt≤2 micron
6. TOLERANCES ON DIA
ISO f7 on the diameter
7.OVALITY
Half of the tolerance ISO f7
8. STRAIGHTNESS
≤0.2MM/M
9 .SURFACE HARDNESS
850-1150HV (vickers 100g)
10. CHROME THICKNESS
20 to 30 micron
11. COHESION
No craks,breaking or detaching after thermic shock(warming up at 300 celsius degrees
and cooling in water)
12 .POROSITY
Test according to ISO 1456/1458 and result yaluation according to ISO 4540 rating 8-10
13. CORROSION RESISTANCE
Test in natural salt spray according to ASTM B 117-120hours
Results evaluation according to ISO 4540 RATING 7-10
14. WELDABILITY
Good
15. PACKING
Anti rust oil to be applied on material and each rod to be packed in paper sleeve
16. CERTIFICATE
All certificate related with material heat treatment and plating is required